Product Details:
|
Product Name: | Vinyl Resin | Application: | Common Metal Overprinting Varnish, Corrosion Resistant Coating For Vessel And Marine, Lacquer For Machinery Shell, Industrial Maintenance Paint, Plastic Lacquer, Can Coating, Leather Coating, Interlamination Adhesive, Magnetic Tape Adhesive, Gravure Printi |
---|---|---|---|
Appearance: | White Or Yellowish Powder | Vinyl Alcohol Content: | 6.0±0.5% |
Vinyl Acetate: | 4.0±1.0% | Hydroxyl Value: | 70-77Mg KOH/g |
Viscosity: | 55~60ml/g | Net Weight: | 25Kg/bag |
High Light: | vinyl chloride vinyl acetate terpolymer resin,vagh vinyl resin |
DAGH Terpolymer Resin The Countertype Of SOLBIN A Used In Interlamination Adhesive
CAS No.: 25086-48-0
Specifications:
No. | Item | Index | Test Method & Criteria | |
1 | Appearance | White powder | By visual | |
2 | Whiteness | ≥80 | GB2913-82 | |
3 |
Composition (%, by Wt) |
Vinyl Acetate | 4.0±1.0 | ISO1159-1978 |
Vinyl Alcohol | 6.0±0.5 | |||
4 |
Reactive Functional Group (Hydroxyl %) |
1.8-2.3 | ||
5 |
Hydroxyl Value (Mg KOH/g) |
70-77 | ISO2554-1974 | |
6 | K Value | 46-52 | GB/T3401-1999 | |
7 |
Viscosity (Ml/g) |
55-60 | GB/T3401-1999 | |
8 | Glass Transition Temp(ºC) | About 79 | GB11998-89 | |
9 | Average Molecular Weight | 27000-30000 | ||
10 |
Grain Size (through 60 mesh) |
100 | GB/T6003.1 | |
11 |
Stacking Density (g/ml) |
≥0.6 | GB20022-2005 | |
12 |
Volatilization (%) |
≤1 | GB/T2914-1999 | |
13 |
Impurity Particle No. (grains/100g) |
≤20 | GB9348-88 | |
14 |
Solubility 25%(MEK : Toluene=1:1)solution |
Colorless, Transparent, No insoluble matter | By visual | |
15 | Countertype | VAGH | DOW | |
E22/48A | Wacker |
Applications:
Mainly applied in common metal overprinting varnish, lacquer for machinery shell, industrial maintenance paint, plastic lacquer, leather coating, interlamination adhesive, magnetic tape adhesive, gravure printing ink for recombination, high grade PU wood paint, metal paint etc.
Solubility:
For DAGH resin, ketone solvents are specially suited, such as ace-tone, MEK, nadone and isophorone. Compared with ketone solvents, ester solvents have lower solubility for DAGH type of resin, such as methyl acetate, ethyl acetate and butyl acetate etc.
For DAGH resin, lower molecular weight is helpful for increasing the solubility of resin and solid content of solution.
Property:
The excellent carrier of pigment used in the inks and coatings, excellent adhesion, used with other film-forming materials to improve the properties of coating, and strengthen adhesion, flexibility, toughness, hardness, chemical resistance etc.
DAGH type of resin can implement cross linking reaction with thermosetting resins (e.g. Isocyanate), the formed film has the following excellences, such as bright, hard and tough, wear resistant, scratch resistant, water resistant and chemical resistant etc.
Compatibility:
DAGH type of terpolymer is miscible with other resins during the course of usage, such as other types of vinyl chloride vinyl acetate copolymer, PVC resin, perchloro-ethylene resin, ketone resins, chloroprene rubber, NBR, polyacrylate, epoxy resin, polyester and petroleum resin etc.
Competitive Advantage:
More appropriate price under the same quality as the one out of China.
Timely and effective service based on quality and technic.
Shorter lead time based on requirements from clients.
Packaging and Storage:
DAGH resin is usually packaged into the craft paper-plastic composite bag lined with plastic film according to 25Kgs per bag.
DAGH resin should be stored in dry place away from sunlight.
Any queries on technology or quality assurance can be inquired to our company.
Should DAGH resin have been kept over the shelf time, it shouldn’t mean the resin is invalid, but the user has to test the relevant properties of DAGH resin and its finished product before using it in bulk.
Contact Person: Mr. Christopher Cao
Tel: 0086 13063757966